A novel surface restoration approach combining plasma gouging with subsequent cold spray deposition is demonstrated in this study. Plasma gouging effectively removes the damaged steel surface, leaving grooves and forming a plasma gouging affected zone up to ~300?µm thick. Within this zone, a hardened martensitic layer with a peak hardness of ~370?HV—almost twice that of the base substrate (~200?HV)—is produced. Following plasma gouging, cold spray deposition is applied to rebuild the surface. Experimental results reveal that cold spray coatings deposited at low energy suffer from delamination, whereas high energy cold spray deposits yield a well-bonded coating. Microstructural analysis further shows that the martensitic layer formed by plasma gouging undergoes dynamic recrystallization during cold spray, reducing the hardness to 317?HV. These findings demonstrate the feasibility of this hybrid method for effective surface restoration of damaged steel components.