Pacific Northwest National Laboratory (PNNL) tested electrolyte coatings from Fuel Cell Enabling Technologies, Inc. (FCET) for use in solid oxide fuel cells (SOFCs). The key technology held by FCET is a process to deposit thin layers of oxide materials, less than 1 um in thickness. The range of possible materials that can be deposited with their method is broad, but this project focused on the gadolinium-doped ceria (GDC) and yttria-stabilized zirconia (YSZ) electrolytes for SOFCs. Thin, gas tight electrolyte membranes have been a long-sought target in SOFC research. The thinner the electrolyte, the lower the cell resistance, and the higher performance of the cell (or the lower the operating temperature). A YSZ thickness of 1 um would be a step change from the state-of-the-art, tape-cast electrolytes (~10 um).
An in-house prototype SOFC stack from FCET was first tested. The sealing geometry of the prototype stack was determined to be problematic, and testing shifted to button cells. Anode-supported solid oxide electrolysis cell (SOEC) button cells without an electrolyte layer were produced at PNNL and sent to FCET for coating with electrolyte. Three cells were tested with a gadolinium-doped ceria (GDC) electrolyte applied via spin coating. GDC was chosen for its conductivity at lower temperatures than YSZ. All three cells failed during initial reduction under hydrogen at 600°C.
Testing then shifted to YSZ, which is the standard SOFC electrolyte. Several button cells were coated with YSZ and examined with scanning electron microscopy (SEM). A promising coating of ~1 mm thickness was observed under SEM. A similarly coated button cell was tested and failed similarly to previous tests during reduction at 600°C.
The YSZ coating appeared dense and uniform in SEM analysis. The roughness of the underlying Ni/YSZ anode is on the order of 1 um, and that may have compromised the gas-tightness of the coating. Further development is warranted to understand and refine the coating process. Thin YSZ applied via this spin-coating technique could be used as a low-cost, drop-in replacement in large-scale SOFC manufacturing processes, improving cell performance and lowering the cost per watt of SOFCs.