Abstract

Rhenium disulfide (ReS2) crystallizes in a distorted 1T' lattice with triclinic symmetry arising from Re–Re dimerization, which produces in-plane anisotropic properties and a dense set of Raman-active modes with mixed atomic displacements. Unlike far-field Raman spectroscopy, which shows strong polarization and orientation dependence, tip-enhanced Raman spectroscopy (TERS) probes out-of-plane Raman tensor components. Here we use 785 nm (1.58 eV) gap-mode TERS to investigate monolayer to four-layer thick ReS2 crystals.. TERS maps and averaged spectra reveal that all modes remain invariant under 90° rotation of the crystal, and the only thickness-dependent feature is the emergence of the multilayer breathing mode. These results demonstrate that TERS yields a crystal-orientation-independent Raman response in ReS2 and provides direct access to Raman tensor components that are not easily accessible in conventional far-field measurements.