Abstract

A high-intensity proton beam exposure with 181 MeV energy has been conducted at Brookhaven Linac Isotope Producer facility on various material specimens for accelerator targetry applications, including titanium alloys as a beam window material. The radiation damage level of the analyzed capsule was 0.25 dpa at the beam center region with an irradiation temperature around 120 oC. Tensile tests showed increased hardness and a large decrease in ductility for the dual a+ß-phase Ti-6Al-4V Grade-5 and Grade-23 extra low interstitial alloys, with the near a-phase Ti-3Al-2.5V Grade-9 alloy still exhibiting uniform elongation of a few % after irradiation. Transmission Electron Microscope analyses on Ti-6Al-4V indicated clear evidence of a high-density of defect clusters with size less than 2 nm in each a-phase grain. The ß-phase grains did not contain any visible defects such as loops or black dots, while the diffraction patterns clearly indicated ?-phase precipitation in an advanced formation stage. The radiation-induced ?-phase transformation in the ß-phase could lead to greater loss of ductility in Ti-6Al-4V alloys in comparison with Ti-3Al-2.5V alloy with less ß-phase.google scho