A survey of the technical literature was performed to summarize the mechanical properties of inorganic components in K Basins sludge. The components included gibbsite, ferrihydrite, lepidocrocite and goethite, hematite, quartz, anorthite, calcite, basalt, Zircaloy, aluminum, and, in particular, irradiated uranium metal and uranium dioxide. Review of the technical literature showed that information on the hardness of uranium metal at irradiation exposures similar to those experienced by the N Reactor fuel present in the K Basins (typically up to 3000 MWd/t) were not available. Measurements therefore were performed to determine the hardness of coupons taken from three irradiated N Reactor uranium metal fuel elements taken from K Basins. Hardness values averaged 30 ± 8 Rockwell C units, similar to values previously reported for uranium irradiated to ~1200 MWd/t. The physical properties of candidate uranium metal and uranium dioxide surrogates were gathered and compared. Surrogates having properties closest to those of irradiated uranium metal appear to be alloys of tungsten. The surrogate for uranium dioxide, present both as particles and agglomerates in actual K Basin sludge, likely requires two materials. Cerium oxide, CeO2, was identified as a surrogate of the smaller UO2 particles while steel grit was identified for the UO2 agglomerates.
Revised: December 8, 2004 |
Published: December 6, 2004