To further understand the suitability of Ni-Cr-base alloys for solid oxide fuel cell (SOFC) interconnect applications, three commercial Ni-Cr-base alloys, Haynes 230, Hastelloy S and Haynes 242 were selected and evaluated for oxidation behavior under different exposure conditions, scale conductivity and thermal expansion. Haynes 230 and Hastelloy S, which have a relatively high Cr content, formed a thin scale mainly comprised of Cr2O3 and (Mn,Cr,Ni)3O4 spinels under SOFC operating conditions, demonstrating excellent oxidation resistance and a high scale electrical conductivity. In contrast, a thick double-layer scale with a NiO outer layer above a chromia-rich substrate was grown on Haynes 242 in moist air or at the air side of dual exposure samples, indicating limited oxidation resistance for the interconnect application. With a face-centered-cubic (FCC) substrate, all three alloys possess a coefficient of thermal expansion (CTE) that is higher than that of candidate ferritic stainless steels, e.g. Crofer22 APU. Among the three alloys, Haynes 242, which is heavily alloyed with W and Mo and contains a low Cr content, demonstrated the lowest average CTE at 13.1x10-6 K-1 from room temperature to 800oC, but it was also observed that the CTE behavior of Haynes 242 was very nonlinear.
Revised: May 11, 2011 |
Published: October 6, 2006
Citation
Yang Z., G. Xia, and J.W. Stevenson. 2006.Evaluation of Ni-Cr-Base Alloys for SOFC Interconnect Applications.Journal of Power Sources 160, no. 2:1104-1110.PNNL-SA-49521.