Abstract

Sodium-ion batteries (SIBs) have attracted extensive interest in the past few years because of the low cost and abundance of sodium resources and hence the potential for grid scale energy storage. Developing low cost electrode materials, particularly anode materials, is the key for further promoting the application of SIBs. Here, we for the first time report a self-standing porous carbon anode directly from natural wood for SIBs, which processes following advantages: (i) ultra-thick carbon anode with a high areal capacity, for example a capacity of 13.6 mAh cm-2 was delivered when the thickness reached 0.85 mm; (ii) low tortuosity, where numerous inherited aligned channels in the wood carbon provide a rapid ion transport path; (iii) porous nature enables a fast ion transfer between the carbon electrode and the electrolyte; (iv) 100% utilization of the wood carbon that conductive additives, binders, and current-collectors are not needed; v) when coupling a Na3V2(PO4)3 cathode with the wood carbon anode, a high capacity of 80 mAh g-1 was obtained at 0.5 C rate (base on cathode) and excellent cycling stability of 300 cycles was also achieved, which demonstrated the promising performance of earth-abundant wood derived carbon material.