Abstract

Cast austenitic stainless steel (CASS) materials are extensively used for many massive primary coolant system components of light water reactors (LWRs) including coolant piping, valve bodies, pump casings, and piping elbows. Many of these components are operated in complex and persistently damaging environments of elevated temperature, high pressure, corrosive environment, and sometimes radiation for long periods of time. Since a large number of CASS components are installed in every nuclear power plant and replacing such massive components is prohibitively expensive, any significant degradation in mechanical properties that affects structural integrity, cracking resistance in particular, of CASS components will raise a serious concern on the performance of entire power plant. The CASS materials for nuclear components are highly corrosion-resistant Fe-Cr-Ni alloys with 300 series stainless steel compositions and mostly austenite (?)–ferrite (d) duplex structures, which result from the casting processes consisting of alloy melting and pouring or injecting liquid metal into a static or spinning mold. Although the commonly used static and centrifugal casting processes enable the fabrication of massive components with proper resistance to environmental attacks, the alloying and microstructural conditions are not highly controllable in actual fabrication, especially in the casting processes of massive components. In the corrosion-resistant Fe-Cr-Ni alloy system, the minor phase (i.e., the d-ferrite phase) is inevitably formed during the casting process, and is in a non-equilibrium state subject to detrimental changes during exposure to elevated temperature and/or radiation. In general, relatively few critical degradation modes are expected within the current design lifetime of 40 years, given that the CASS components have been processed properly. It has been well known, however, that both the thermal aging and the neutron irradiation can cause degradation of static and impact toughness in the cast stainless steels, and if combined with any flaws formed during the fabrication process or in service, the thermal degradation in CASS components can be a serious concern for the integrity of the power plant. On the integrity of the CASS components during the extended lifetime of 60 years or longer, no conclusive prediction has been possible, primarily because no direct experience with these materials currently exists, and the aging behavior of CASS alloys still remains largely uncertain. The ongoing research for CASS aging, as part of the LWRS Program/Materials Aging and Degradation Pathway, is an integrated research using holistic experimental and modeling means to provide both the scientific understanding on the aging and failure phenomena and the practical models to predict the degree of property degradation.