Abstract

The dissolution of Tc(IV) sulfide and concurrent transformation of sulfidated ZVI during 2 oxidation were examined. Kinetic data obtained with 10 mL batch reactors showed that Tc(VII) 3 reduced by sulfidated nZVI has significantly slower reoxidation rates than Tc(VII) reduced by 4 nZVI only. In a 50 mL batch reactor, initial inhibition of Tc(IV) dissolution was apparent and 5 lasted until 120 hours at S/Fe = 0.112, presumably due to the redox buffer capacity of FeS. This 6 is evidenced by the parallel trends in oxidation-reduction potentials (ORP) and Tc dissolution 7 kinetics. M?ssbauer spectra and micro X-ray diffraction of S/Fe = 0.112 suggested the 8 persistence of FeS after 24-h oxidation although X-ray photoelectron spectroscopy indicated 9 substantial surface oxidation. After 120-h oxidation, all characterizations showed complete 10 oxidation of FeS, which further indicates that FeS inhibits Tc oxidation. X-ray absorption 11 spectroscopy for S/Fe = 0.011 showed significantly increasing percentage of TcS2 in the solid 12 phase after 24-h oxidation, indicating TcS2 is more resistant to oxidation than TcO2. At S/Fe = 13 0.112, the XAS results revealed significant transformation of Tc speciation from TcS2 to TcO2 14 after 120-h oxidation at S/Fe = 0.112. Given that no apparent Tc dissolution occurred during this 15 period, the speciation transformation might play a secondary role in hindering Tc oxidation, 16 especially as redox buffer capacity approached depletion.