Abstract

The composition of the solid electrolyte interphase (SEI) layers associated with a high performance Cu|Li cell using lithium bis(fluorosulfonyi)imide (LiFSI) in 1,2-dimethoxyethane (DME) as electrolyte is determined by a multinuclear (6Li, 19F, 13C and 1H) solid-state MAS NMR study at high magnetic field (850 MHz). This cell can be cycled at high rates (4 mA•cm-2) for more than 1000 cycles with no increase in the cell impedance at high Columbic efficiency (average of 98.4%) in a highly concentrated LiFSI-DME electrolyte (4 M). LiFSI, LiF, Li2O2 (and/or CH3OLi), LiOH, Li2S and Li2O are observed in the SEI and validated by comparing with the spectra acquired on standard compounds and literature reports. To gain further insight into the role of the solute and its concentration dependence on the formation of SEIs while keeping the solvent of DME unchanged, the SEIs from different concentrations of LiFSI-DME and lithium bis(trifluoromethanesulfonyl)imide (LiTFSI)-DME electrolyte are also investigated. It is found that LiF, a lithiated compound with superior mechanical strength and good Li+ ionic conductivity, is observed in the concentrated 4.0 M LiFSI-DME and the 3.0 M LiTFSI-DME systems but not in the diluted 1.0 M LiFSI-DME system. Li2O exists in both low and high concentration of LiFSI-DME while no Li2O is observed in the LiTFSI system. Furthermore, the dead metallic Li is reduced in the 4 M LiFSI-DME system compared with that in the 1 M LiFSI-DME system. Quantitative 6Li MAS results indicate that the SEI associated with the 4 M LiFSI-DEME is denser or thicker than that of the 1 M LiFSI-DME and the 3 M LiTFSI-DME systems. These findings are likely the reasons for explaining the high electrochemical performance associated with the high concentration LiFSI-DME system.