Abstract

A series of NH3 temperature-programmed desorption (TPD) spectra was taken after the NH3 dose at 70 K on rutile TiO2(110)-1×1 surfaces with the oxygen vacancy (VO) concentrations of ~0% (p-TiO2) and 5% (r-TiO2), respectively, to study the effect of VO’s on the desorption energy of NH3 as a function of the coverage, ?. Our results show that at zero coverage limit, the desorption energy of NH3 on r-TiO2 is 115 kJ/mol, which is 10 kJ/mol less than that on p-TiO2. The desorption energy from the Ti4+ sites decreases with increasing ? due to the repulsive NH3 - NH3 interactions and approaches ~ 55 kJ/mol upon the saturation of Ti4+ sites (? = 1 monolayer, ML) on both p- and r-TiO2. The absolute saturation coverage is determined to be about 10% smaller on r-TiO2 than that on p-TiO2. Further, the trailing edges of the NH3 TPD spectra on the hydroxylated TiO2(110) (h-TiO2) appear to be the same as that on r-TiO2 while those on oxidized TiO2(110) (o-TiO2) shift to higher temperatures. We present the detailed analysis of the results and reconcile the observed differences based on the repulsive adsorbate-adsorbate interactions between neighboring NH3 molecules and the surface charge associated with the presence of VO’s. Besides NH3, no other reaction products are observed in the TPD spectra.