Abstract

The passivation behavior of Yucca Mountain Repository rock bolt carbon steel in deaerated 3.5% NaCl solution containing SiO2_3 and HCO_3 ions was investigated by potentiodynamic polarization, electrochemical impedance spectroscopy, scanning electron microscopy, and X-ray photoelectron spectroscopic methods. Polarization results indicate that combinations of silicate and bicarbonate anions decrease the passive current density and raise the pitting potential. XPS results indicate the enrichment of silica at passive potentials and the formation of mixed FeCO3 and silica film at lower potentials. This change in film composition was responsible for the changes in corrosion rate at lower and higher potentials. XPS results also support the thermodynamic data with regard to the occurrence of second oxidation peak observed in the polarization curves to be due to the oxidation of FeCO3 to Fe2O3