Abstract

Future advances and usage of all-organic polymeric materials with permanent void spaces and high surface areas, in applications such as separations or as supports, depends heavily on the development of processing techniques to produce complex geometry objects. Here, the high free volume glassy microporous polymer PIM-1 was fabricated, as a major component in a polymer blend, into complex and customizable 3D objects by fused filament fabrication (FFF). PIM-1 was found to be compatible with polycaprolactone (PCL) and polylactic acid (PLA) and thus could be processed by extrusion into filaments with high loadings of PIM-1 (50% by mass). Ternary PCL/PLA/PIM-1 composite filaments provided an optimal balance of durability and melt flow characteristics for consistent FFF 3D printing of intricate structures. As printed, the micropores of PIM-1 were blocked and inaccessible to N2 during sorption experiments; however, the ternary composite structures displayed significant meso- and macroporosity and nanostructured phase separation. Postprinting immersion in 3-chloro-1-propanol was identified to selectively remove PCL within the composites, re-expose the characteristic micropores of PIM-1, and retain the macrostructure of the printed object. After postprinting treatments, specific surface areas by the Brunauer–Emmett–Teller method (as high as 460 m2 g–1) were found to directly correlate with the PCL content originally present. The extrusion-based processing methodology provides a new approach for production of intrinsically porous polymer objects in custom and complex shapes by reinforcement with thermoplastics (PCL and PLA).