Nanocomposite of TiO2 nanotubes (TiO2NTs) and multiwalled carbon nanotubes (MWCNTs) has been synthesized by a hydrothermal method and firstly used in photocatalytic hydrogen production. The obtained TiO2 NTs/MWCNTs composites were characterized by X-ray diffraction, transmission electron microscopy, Raman spectrum and ultraviolet-visible diffuse reflectance spectroscopy. The experimental results revealed that the MWCNTs were decorated with well dispersed anatase TiO2 nanotubes with a diameter of 8-15 nm. A slight blue shift and weak symmetry was observed for the strongest Raman peak which resulted from strain gradients originating from interface integration between TiO2 nanotubes and MWCNTs. The photocatalytic activity of the as-prepared samples was evaluated by hydrogen evolution from water splitting using Na2S and Na2SO3 as sacrificial reagents under UV-vis light irradiation. Enhanced photocatalytic activity compared with P25 has been observed for the resulted samples. The nanocomposite with optimized MWCNTs content of 1% displayed a hydrogen production rate of 161 u mol/h/g. Good photocatalytic stability of the as-synthesized samples was observed as well.
Revised: July 30, 2012 |
Published: March 1, 2012
Citation
Li H., X. Zhang, X. Cui, and Y. Lin. 2012.TiO2 Nanotubes/MWCNTs Nanocomposite Photocatalysts: Synthesis, Characterization and Photocatalytic Hydrogen Evolution Under UV-Vis Light Illumination.Journal of Nanoscience and Nanotechnology 12, no. 3:1806-1811.PNNL-SA-84850.doi:10.1166/jnn.2012.5161